Carefully crafted water-based ecological resin for you!
ZF8326C
ZF8326C Waterborne Epoxy Resin
Product Characteristics
This product is a one-component epoxy resin emulsion for metal coating. Due to its good adhesion and water resistance on metal, it can produce a coating with excellent rust prevention performance on metal substrates. It is especially suitable for one-component waterborne rust-proof primers for metal.
Product Applications
1. Metal anti-corrosion coatings
2. Industrial coatings
3. Coatings for machinery products
4. Marine coatings
Main Features
1. Can be used as a one-pack system;
2. Good corrosion resistance;
3. Good water resistance;
4. Good pigment dispersibility and mechanical dispersion stability;
5. Good adhesion;
6. Can be used with amino resins to produce waterborne amino baking paint
Physical Parameters
ZF8326C Waterborne Epoxy Resin
Resin Type | Epoxy resin dispersion |
Appearance | Milky white liquid |
Solid Content (%) | 37.0-40.0 |
Viscosity (mpa.s) | 500-5000 |
PH | 8.0-9.0 |
Recommended Formulation:
ZF8326C Anti-corrosion Primer (Iron Red) Formulation
Iron Red Paste Grinding
Function | Composition | Supplier | Dosage |
Diluent | Pure water | - | 40.3 |
Dispersant | Tego 760W | Evonik | 2.1 |
Defoamer | BYK-024 | BYK | 0.5 |
Add in sequence, low-speed dispersion (500-800 rpm) for 5-10 minutes. After uniform dispersion, add the following materials in sequence. | |||
Iron Oxide Red | R01 | Zhuojie Chemical | 20.8 |
Rust-proof pigment | Hangzhou Fenghong | 15.6 | |
Filler | Precipitated Barium Sulfate | Guangfu (Jiaoling) | 5.2 |
Filler | Sericite powder | Chuzhou Gree | 15.6 |
Total | 100.0 | ||
High-speed dispersion (1500 rpm and above)/milling for more than 30 minutes, until the fineness is below 30 μm |
Paint Adjustment
Function | Composition | Supplier | Dosage |
Color Paste | Iron Red Paste | 38.3 | |
Film-forming resin | ZF8326C | Zhongfang | 59.6 |
Wetting agent | BYK-346 | BYK | 0.5 |
Defoamer | BYK-024 | BYK | 0.1 |
Anti-flash rust agent | X-515 | HALOX | 1.0 |
Thickener | WT-105A | Elementis | 0.5 |
Total | 100.0 | ||
Add in sequence under low-speed dispersion, disperse evenly, and filter the material with a 120-mesh filter cloth. |
Coating Conditions:
Main agent/pure water = 100/appropriate amount
Drying: 160℃ x 20 minutes baking
Film thickness: 30-40 μm
Substrate: Tinplate/cold-rolled steel sheet
Film Properties:
Pencil hardness (China pencil): 2H
Cross-hatch adhesion (1mm): 100/100
Salt spray resistance: ≥ 200H
ZF8326C Anti-corrosion Primer (White) Formulation
White Paste Grinding
Function | Composition | Supplier | Dosage |
Film-forming resin | ZF8326C | Zhongfang | 23 |
Thinner | Pure water | - | 18.3 |
Dispersant | BYK-2080 | BYK | 1.8 |
Defoamer | BYK-024 | BYK | 0.5 |
Add in sequence, low-speed dispersion (500-800 rpm) for 5-10 minutes. After uniform dispersion, add the following raw materials in sequence | |||
Titanium dioxide | R706 | DuPont | 41.2 |
Rust-proof pigment | Zhejiang Fenghong | 13.7 | |
Organic corrosion inhibitor | RZ | Heubach | 1.5 |
Total | 100.0 | ||
High-speed dispersion (1500 rpm and above)/milling for more than 30 minutes, until the fineness is below 30 μm |
Paint Adjustment
Function | Composition | Supplier | Formulation |
Color Paste | White paste | 42.9 | |
Film-forming resin | ZF8326C | Zhongfang | 49.0 |
Amino resin | 325 | Cyanate | 2.4 |
Coloring agent | WE3323 | BASF | 0.5 |
Defoamer | BYK-024 | BYK | 0.2 |
Anti-flash rust agent | ASCOTRAN-H14 | ASCOTEC | 0.5 |
Rheology modifier | AQ-633E | DISPARLON | 1.0 |
Thickener | WT-105A | Elementis | 0.3 |
Diluent | Pure water | - | 3.2 |
Total | 100.0 |
Coating conditions
Main agent/pure water = 100/appropriate amount
Drying: 160℃ x 20 minutes baking
Film thickness: 30-40μm
Substrate: Tinplate/cold-rolled steel sheet
Film properties
Pencil hardness (China pencil): 2H
Cross-hatch adhesion (1mm): 100/100
Salt spray resistance: ≥ 200H
Packaging and transportation
Net weight 200KG/barrel, HDPE barrel packaging. Store in a cool, dry, well-ventilated place, keep the container sealed. Shelf life is six months.