PU186-2
PU186-2 Alkali-Resistant High-Elastic Waterborne Polyurethane Resin
Product Description
This product is a water dispersion copolymerized from aliphatic isocyanate and special polyether polyol. The film is transparent, bright, and smooth. Compared with similar resins, it shows excellent elongation, hydrolysis resistance, weather resistance, water resistance, and low-temperature resistance.
Physicochemical Indicators
▪ Appearance | : | Milky white liquid |
▪ Viscosity (mpa.s) | : | 50-150 |
▪ Acidity/Alkalinity | : | 7-8 |
▪ Solids content (%) | : | 40±1 |
▪ Ionicity | : | Anionic |
▪ Elongation | : | 600% |
Performance Characteristics
▪ Maintains good elasticity at low temperatures
▪ Excellent weather resistance, alkali resistance, and water resistance
▪ Free of APEO, formaldehyde, and heavy metals
Application Range
Film-forming resin for leather finishing and plastics industries
Precautions
▪ When used as an adhesive, a certain amount of water-based NC0 type curing agent or water-based crosslinking agent can be added to increase the bonding strength
▪ This product can be blended with other anionic or non-ionic PA and PU resins
Packaging and Transportation
▪ This product is a water-based emulsion, non-flammable, and non-explosive. It is transported as non-dangerous goods.
▪ This product should be transported and stored at 5-35℃, with a shelf life of six months. Net weight 50Kg or 125Kg plastic drum packaging.
Remarks
This description is based on practical certified data. Due to the different user conditions and product requirements, please conduct experiments or contact our technical department to determine the suitable process for your factory.